The thermal stability of a 80-vol.% HfB2 + 20 vol.% MoSi2 Composite is tested under oxidizing environment. Oxidation tests are carried out in flowing synthetic air in a TG equipment from 1000 to 1400 ◦C with exposure time of 30 h. At temperatures ≥1200 ◦C the silica resulting from oxidation of molybdenum disilicide seals the sample surface, preventing hafnium diboride from fast degradation. Analysis of the kinetics is carried out through fitting of the thermogravimetric curves. Between 1200 and 1400 ◦C, the kinetic curves deviate from a parabolic behaviour, being more close to a logarithmic–parabolic behaviour

Oxidation behaviour of a pressureless sintered HfB2–MoSi2 composite

BALBO, Andrea
Secondo
;
2009

Abstract

The thermal stability of a 80-vol.% HfB2 + 20 vol.% MoSi2 Composite is tested under oxidizing environment. Oxidation tests are carried out in flowing synthetic air in a TG equipment from 1000 to 1400 ◦C with exposure time of 30 h. At temperatures ≥1200 ◦C the silica resulting from oxidation of molybdenum disilicide seals the sample surface, preventing hafnium diboride from fast degradation. Analysis of the kinetics is carried out through fitting of the thermogravimetric curves. Between 1200 and 1400 ◦C, the kinetic curves deviate from a parabolic behaviour, being more close to a logarithmic–parabolic behaviour
2009
D., Sciti; Balbo, Andrea; A., Bellosi
File in questo prodotto:
File Dimensione Formato  
Sciti-D._Oxidation-behaviour-of-a-pressureless-sintered-HfB2-MoSi2-composite_J.-Eur.-Ceram.-Soc._2009_29_9_1809_1815.pdf

solo gestori archivio

Descrizione: Full text editoriale
Tipologia: Full text (versione editoriale)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 1.33 MB
Formato Adobe PDF
1.33 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/534425
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 61
  • ???jsp.display-item.citation.isi??? 55
social impact