Co-Cu multilayer granular films deposited onto SiO2/Si substrates have been submitted to thermal treatments in scanning mode. Their magnetisation, resistance and magnetoresistance have been studied after applying two different heating rates. The analysis of experimental data points out that only with the lower heating rate the properties of the films are strongly modified. In this case, indeed, XPS measurements show the presence of interdiffusion between atomic species of the substrate and metallic species inside the film. XPS data are presented to show the modifications in composition and chemical environment produced by thermal treatments. (C)1999 Acta Metallurgica Inc.

Effects of atomic diffusion processes in Co-Cu multilayer granular films

BISERO, Diego;BORDIN, Giorgio;RONCONI, Franco;SPIZZO, Federico;
1999

Abstract

Co-Cu multilayer granular films deposited onto SiO2/Si substrates have been submitted to thermal treatments in scanning mode. Their magnetisation, resistance and magnetoresistance have been studied after applying two different heating rates. The analysis of experimental data points out that only with the lower heating rate the properties of the films are strongly modified. In this case, indeed, XPS measurements show the presence of interdiffusion between atomic species of the substrate and metallic species inside the film. XPS data are presented to show the modifications in composition and chemical environment produced by thermal treatments. (C)1999 Acta Metallurgica Inc.
1999
Bisero, Diego; Bordin, Giorgio; M., Minelli; Ronconi, Franco; Spizzo, Federico; A., Baraldi; S., Lizzit; G., Paolucci; L., Pareti; G., Turilli...espandi
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/520374
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact