Effect of Al2O3-SiC powder addition on the microstructural and mechanical properties of dissimilar AA2024-AA7075 FSW joints

In the last years, dissimilar joints produced by friction stir welding are getting attention due to their excellent properties and their high potential in structural components. However, process parameters, including the addition of a reinforcement on the weld line to improve mechanical performance, must be well established to obtain sound quality joints. In the present investigation fourteen dissimilar AA2024-AA7075 friction stir butt welded joints were performed with and without the addition of Al2O3-SiC powders. The microstructure of the samples was studied by optical and scanning electron microscopy in order to assess the main microstructural features. Moreover, tensile and hardness tests were performed to identify the input parameters suitable to gain the best mechanical and microstructural properties.

Negli ultimi anni la realizzazione di giunti dissimili mediante tecnica friction stir welding sta acquisendo sempre maggiore importanza in virtù sia delle loro eccellenti proprietà sia del loro elevato potenziale di utilizzo in componenti strutturali. Tuttavia, per ottenere giunti di buona qualità i parametri di processo necessitano di essere ottimizzati, soprattutto nel caso dell’aggiunta di particelle di rinforzo sulla linea di saldatura. Nella memoria sono presentati alcuni risultati riguardanti la realizzazione mediante friction stir welding di quattordici giunti dissimili del tipo AA2024-AA7075 con e senza l’aggiunta di polveri Al2O3-SiC. La microstruttura dei campioni è stata studiata mediante microscopia ottica ed elettronica a scansione. Inoltre, sono presentati i risultati di prove di durezza e di prove di trazione effettuate al fine di individuare i parametri più idonei ad ottenere le migliori proprietà microstrutturali e meccaniche.