A green, effective methodology for the preparation of water-based dispersions of poly(lactic acid) (PLA) for coating purposes is herein presented. The procedure consists of two steps: In the first one, an oil-in-water emulsion is obtained by mixing a solution of PLA in ethyl acetate with a water phase containing surfactant and stabilizer. Different homogenization methods as well as oil/water phase ratio, surfactant and stabilizer combinations were screened. In the second step, the quantitative evaporation of the organic provides water dispersions of PLA that are stable, at least, over several weeks at room temperature or at 4 °C. Particle size was in the 200–500 nm range, depending on the preparation conditions, as confirmed by scanning electron microscope (SEM) analysis. PLA was found not to suffer significant molecular weight degradation by gel permeation chromatography (GPC) analysis. Furthermore, two selected formulations with glass transition temperature (Tg) of 51 °C and 34 °C were tested for the preparation of PLA films by drying in PTFE capsules. In both cases, continuous films that are homogeneous by Fourier-transform infrared spectroscopy (FT-IR) and SEM observation were obtained only when drying was performed above 60 °C. The formulation with lower Tg results in films which are more flexible and transparent.

Preparations of poly(Lactic acid) dispersions in water for coating applications

Belletti G.
Primo
Writing – Original Draft Preparation
;
Buoso S.;Bortolini O.
Penultimo
Supervision
;
Bertoldo M.
Ultimo
Conceptualization
2021

Abstract

A green, effective methodology for the preparation of water-based dispersions of poly(lactic acid) (PLA) for coating purposes is herein presented. The procedure consists of two steps: In the first one, an oil-in-water emulsion is obtained by mixing a solution of PLA in ethyl acetate with a water phase containing surfactant and stabilizer. Different homogenization methods as well as oil/water phase ratio, surfactant and stabilizer combinations were screened. In the second step, the quantitative evaporation of the organic provides water dispersions of PLA that are stable, at least, over several weeks at room temperature or at 4 °C. Particle size was in the 200–500 nm range, depending on the preparation conditions, as confirmed by scanning electron microscope (SEM) analysis. PLA was found not to suffer significant molecular weight degradation by gel permeation chromatography (GPC) analysis. Furthermore, two selected formulations with glass transition temperature (Tg) of 51 °C and 34 °C were tested for the preparation of PLA films by drying in PTFE capsules. In both cases, continuous films that are homogeneous by Fourier-transform infrared spectroscopy (FT-IR) and SEM observation were obtained only when drying was performed above 60 °C. The formulation with lower Tg results in films which are more flexible and transparent.
2021
Belletti, G.; Buoso, S.; Ricci, L.; Guillem-Ortiz, A.; Aragon-Gutierrez, A.; Bortolini, O.; Bertoldo, M.
File in questo prodotto:
File Dimensione Formato  
polymers-13-02767.pdf

accesso aperto

Descrizione: versione editoriale
Tipologia: Full text (versione editoriale)
Licenza: Creative commons
Dimensione 3.69 MB
Formato Adobe PDF
3.69 MB Adobe PDF Visualizza/Apri

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2464899
Citazioni
  • ???jsp.display-item.citation.pmc??? 2
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 13
social impact