Ultrathin layers of gold, from 2 to 25 nm of nominal coverage, have been deposited on sodium-alginate biopolymer foils applying two alternative approaches: low power sputtering and thermal evaporation. The morphology of the deposited layers was obtained by means of atomic force microscopy. In the early stages of growth, thermal evaporation gives rise to a top surface resembling the underlying substrate, whereas low power sputtering produces a topography characterized by smoother areas. This indicates that the film growth occurs in different ways. X-ray photoelectron spectroscopy with two photon energies, corresponding to Al Kα and Ag Lα photons, was used to get information on the chemistry at the interface and on the degree of intermixing between Au and sodium-alginate. While no chemical modifications with respect to the bare materials could be detected, the evolution of the intensities of the relevant core levels of Au and sodium alginate (Au 4f and Na 1s in particular) indicated a strong intermixing in the case of films deposited by low power sputtering. This is further supported by optical measurements. The observed behaviour can be correlated with the enhanced adhesion of sputtered films compared to thermally evaporated ones.

Understanding adhesion of gold conductive films on sodium-alginate by photoelectron spectroscopy

Maccagnani P.
Secondo
Investigation
;
Bertoldo M.
Conceptualization
;
2019

Abstract

Ultrathin layers of gold, from 2 to 25 nm of nominal coverage, have been deposited on sodium-alginate biopolymer foils applying two alternative approaches: low power sputtering and thermal evaporation. The morphology of the deposited layers was obtained by means of atomic force microscopy. In the early stages of growth, thermal evaporation gives rise to a top surface resembling the underlying substrate, whereas low power sputtering produces a topography characterized by smoother areas. This indicates that the film growth occurs in different ways. X-ray photoelectron spectroscopy with two photon energies, corresponding to Al Kα and Ag Lα photons, was used to get information on the chemistry at the interface and on the degree of intermixing between Au and sodium-alginate. While no chemical modifications with respect to the bare materials could be detected, the evolution of the intensities of the relevant core levels of Au and sodium alginate (Au 4f and Na 1s in particular) indicated a strong intermixing in the case of films deposited by low power sputtering. This is further supported by optical measurements. The observed behaviour can be correlated with the enhanced adhesion of sputtered films compared to thermally evaporated ones.
2019
Capelli, R.; Maccagnani, P.; Dinelli, F.; Murgia, M.; Bertoldo, M.; Montecchi, M.; Doyle, B. P.; Carleschi, E.; Pasquali, L.
File in questo prodotto:
File Dimensione Formato  
1-s2.0-S0040609019305632-main.pdf

solo gestori archivio

Descrizione: versione editoriale
Tipologia: Full text (versione editoriale)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 4.17 MB
Formato Adobe PDF
4.17 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2414338
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 7
  • ???jsp.display-item.citation.isi??? 7
social impact