This paper reports the effects of thermal aging between 650 and 850 °C on the localized corrosion behavior of lean duplex stainless steel (LDSS 2404). Critical pitting temperature (CPT) and double loop electrochemical potentiokinetic reactivation (DL-EPR) tests were performed. The localization of pitting attack and intergranular corrosion (IGC) attack after DL-EPR was investigated by optical (OM) and scanning electron microscopy (SEM) and by focused ion beam (FIB) coupled to SEM. Thermal aging caused the precipitation of mainly chromium nitrides at grain boundaries. Aging at 650 °C or short aging times (5 min) at 750 °C caused nitride precipitation mainly at α/α grain boundaries as a result of fast diffusion of chromium in this phase. Aging at 850 °C or aging times from 10 to 60 min at 750 °C also allowed the precipitation at the α/γ interface. Nitrides at γ/γ grain boundaries were observed rarely and only after long aging times (60 min) at 850 °C. Electrochemical tests showed that in as-received samples, pitting attack only affected the α phase. Conversely, in aged samples, pitting and IGC attack were detected close to nitrides in correspondence of α/α and α/γ grain boundaries depending on aging temperatures and times.

Investigation on the Corrosion Behavior of Lean Duplex Stainless Steel 2404 after Aging within the 650–850°C Temperature Range

Federica Zanotto
Primo
;
Vincenzo Grassi
Secondo
;
Andrea Balbo;Fabrizio Zucchi
Penultimo
;
Cecilia Monticelli
Ultimo
2019

Abstract

This paper reports the effects of thermal aging between 650 and 850 °C on the localized corrosion behavior of lean duplex stainless steel (LDSS 2404). Critical pitting temperature (CPT) and double loop electrochemical potentiokinetic reactivation (DL-EPR) tests were performed. The localization of pitting attack and intergranular corrosion (IGC) attack after DL-EPR was investigated by optical (OM) and scanning electron microscopy (SEM) and by focused ion beam (FIB) coupled to SEM. Thermal aging caused the precipitation of mainly chromium nitrides at grain boundaries. Aging at 650 °C or short aging times (5 min) at 750 °C caused nitride precipitation mainly at α/α grain boundaries as a result of fast diffusion of chromium in this phase. Aging at 850 °C or aging times from 10 to 60 min at 750 °C also allowed the precipitation at the α/γ interface. Nitrides at γ/γ grain boundaries were observed rarely and only after long aging times (60 min) at 850 °C. Electrochemical tests showed that in as-received samples, pitting attack only affected the α phase. Conversely, in aged samples, pitting and IGC attack were detected close to nitrides in correspondence of α/α and α/γ grain boundaries depending on aging temperatures and times.
2019
Zanotto, Federica; Grassi, Vincenzo; Balbo, Andrea; Zucchi, Fabrizio; Monticelli, Cecilia
File in questo prodotto:
File Dimensione Formato  
metals-09-00529.pdf

solo gestori archivio

Descrizione: Full text editoriale
Tipologia: Full text (versione editoriale)
Licenza: Creative commons
Dimensione 6.52 MB
Formato Adobe PDF
6.52 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2405718
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 5
social impact