The fabrication of homogeneously doped germanium layers characterized by total electrical activation is currently a hot topic in many fields, such as microelectronics, photovoltaics, optics and radiation detectors. Phosphorus spin-on-doping technique has been implemented on Ge wafers, by developing a protocol for the curing process and subsequent diffusion annealing for optimal doping. Parameters such as relative humidity and curing time turned out to affect the surface morphology, the degree of reticulation reached by the dopant source and the amount of dopant available for diffusion. After spike annealing in a conventional furnace, diffusion profiles and electrical properties have been measured. Ge loss from the surface during high-temperature annealing, due to diffusion into the source film, has been observed and quantified.

Optimal process parameters for phosphorus spin-on-doping of germanium

BOLDRINI, Virginia;CAMATTARI, Riccardo;
2017

Abstract

The fabrication of homogeneously doped germanium layers characterized by total electrical activation is currently a hot topic in many fields, such as microelectronics, photovoltaics, optics and radiation detectors. Phosphorus spin-on-doping technique has been implemented on Ge wafers, by developing a protocol for the curing process and subsequent diffusion annealing for optimal doping. Parameters such as relative humidity and curing time turned out to affect the surface morphology, the degree of reticulation reached by the dopant source and the amount of dopant available for diffusion. After spike annealing in a conventional furnace, diffusion profiles and electrical properties have been measured. Ge loss from the surface during high-temperature annealing, due to diffusion into the source film, has been observed and quantified.
Boldrini, Virginia; Carturan, Sara Maria; Maggioni, Gianluigi; Napolitani, Enrico; Napoli, Daniel Ricardo; Camattari, Riccardo; De Salvador, Davide
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2371368
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 20
  • ???jsp.display-item.citation.isi??? 18
social impact