This paper reports the results obtained in the evaluation of the corrosion resistance and mechanical characterization for SLM fabrication of endoprosthetic ankle devices. The corrosion behavior was monitored by recording the EIS spectra and polarization curves during 15 days of immersion in PBS (phosphate buffer saline) solution at pH 7.4 and pH 4, simulating the compositions of the body fluids under normal and inflammatory conditions, respectively. The surface of the samples was characterized by SEM / EDS analysis. Finally, by considering mechanical resistance, corrosion resistance and manufacturing time, a differentiated process parameter strategy was proposed for bulk and surface fabrication
Corrosion resistance and mechanical characterization of ankle prostheses fabricated via selective laser melting
BALBO, Andrea;MONTICELLI, Cecilia;
2017
Abstract
This paper reports the results obtained in the evaluation of the corrosion resistance and mechanical characterization for SLM fabrication of endoprosthetic ankle devices. The corrosion behavior was monitored by recording the EIS spectra and polarization curves during 15 days of immersion in PBS (phosphate buffer saline) solution at pH 7.4 and pH 4, simulating the compositions of the body fluids under normal and inflammatory conditions, respectively. The surface of the samples was characterized by SEM / EDS analysis. Finally, by considering mechanical resistance, corrosion resistance and manufacturing time, a differentiated process parameter strategy was proposed for bulk and surface fabricationI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.