Nanocrystalline TiO2 photocatalysts were synthesized in mild conditions by thermohydrolysis of TiOSO4 in water at 100 °C and post-calcination treatment at various temperatures. The TiO2 powders were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, specific surface area determinations, scanning electron microscopy and electron paramagnetic resonance measurements. The photoactivity of the samples was tested employing the photodegradation of 4-nitrophenol in liquid–solid regimen and the photooxidation of gaseous 2-propanol. The best results were obtained with the powder calcined at 600 °C for 10 h. Surprisingly, the not calcined sample was the most active for the abatement of NOx under irradiation.

Preparation and Photoactivity of Nanocrystalline TiO2 Powders Obtained by Thermohydrolysis of TiOSO4

AMADELLI, Rossano;SAMIOLO, Luca
2013

Abstract

Nanocrystalline TiO2 photocatalysts were synthesized in mild conditions by thermohydrolysis of TiOSO4 in water at 100 °C and post-calcination treatment at various temperatures. The TiO2 powders were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, specific surface area determinations, scanning electron microscopy and electron paramagnetic resonance measurements. The photoactivity of the samples was tested employing the photodegradation of 4-nitrophenol in liquid–solid regimen and the photooxidation of gaseous 2-propanol. The best results were obtained with the powder calcined at 600 °C for 10 h. Surprisingly, the not calcined sample was the most active for the abatement of NOx under irradiation.
2013
Di Paola, A.; Bellardita, M.; Palmisano, L.; Amadelli, Rossano; Samiolo, Luca
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2095213
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 14
  • ???jsp.display-item.citation.isi??? 12
social impact