Detection of the dynamic magnetic behavior of the antiferromagnet in exchange-coupled NiFe/IrMn bilayers

The magnetothermal behavior of antiferromagnetic IrMn layers of different thickness (3, 6, 10 nm) has been studied exploiting the exchange coupling with a ferromagnetic 5nm-thick NiFe layer. A procedure has been devised for the measurement of the magnetization of the NiFe/IrMn bilayers as a function of temperature and time at different values of an external magnetic field, Hinv, antiparallel to the unidirectional exchange anisotropy. This analysis allows one to probe the effective distribution of anisotropy energy barriers of the antiferromagnetic phase, as sensed by the ferromagnetic layer. Two magnetic regimes have been distinguished. At temperature T < 100 K, the interfacial IrMn spins are frozen in a glassy state and are collectively involved in the exchange coupling with the NiFe spins. At T ~ 100 K the collective state breaks up; thus, above this temperature, only the interfacial IrMn spins which are tightly polarized by the IrMn nanograins, forming the bulk of the layer, are effectively involved in the exchange coupling mechanism. Due to that, for T > 100 K the exchange coupling is ruled by the anisotropy energy barriers of the bulk IrMn nanograins, namely by the layer thickness. The thermal evolution of the exchange field and of the coercivity in the three samples is coherently explained in the framework of this description of the dynamic magnetic behavior of the IrMn phase.