This paper describes the results of the round robin experiment "Bead production technologies" carried out during the COST 840 action "Bioencapsulation Innovation and Technologies" within the 5th Framework Program of the European Community. In this round robin experiment, calcium alginate hydrogel beads with the diameter of (800 ± 100) μm were produced by the most common bead production technologies using 0.5-4 mass % sodium alginate solutions as starting material. Dynamic viscosity of the alginate solutions ranged from less than 50 mPa s up to more than 10000 mPa s. With the coaxial air-flow and electrostatic enhanced dropping technologies as well as with the JetCutter technology in the soft-landing mode, beads were produced from all alginate solutions, whereas the vibration technology was not capable to process the high-viscosity 3 % and 4 % alginate solutions. Spherical beads were generated by the electrostatic and the JetCutter technologies. Slightly deformed beads were obtained from high-viscosity alginate solutions using the coaxial airflow and from the 0.5 % and 2 % alginate solutions using the vibration technology. The rate of bead production using the JetCutter was about 10 times higher than with the vibration technology and more than 10000 times higher than with the coaxial air-flow and electrostatic technology. © 2008 Institute of Chemistry, Slovak Academy of Sciences.

Comparison of different technologies for alginate beads production

NASTRUZZI, Claudio;
2008

Abstract

This paper describes the results of the round robin experiment "Bead production technologies" carried out during the COST 840 action "Bioencapsulation Innovation and Technologies" within the 5th Framework Program of the European Community. In this round robin experiment, calcium alginate hydrogel beads with the diameter of (800 ± 100) μm were produced by the most common bead production technologies using 0.5-4 mass % sodium alginate solutions as starting material. Dynamic viscosity of the alginate solutions ranged from less than 50 mPa s up to more than 10000 mPa s. With the coaxial air-flow and electrostatic enhanced dropping technologies as well as with the JetCutter technology in the soft-landing mode, beads were produced from all alginate solutions, whereas the vibration technology was not capable to process the high-viscosity 3 % and 4 % alginate solutions. Spherical beads were generated by the electrostatic and the JetCutter technologies. Slightly deformed beads were obtained from high-viscosity alginate solutions using the coaxial airflow and from the 0.5 % and 2 % alginate solutions using the vibration technology. The rate of bead production using the JetCutter was about 10 times higher than with the vibration technology and more than 10000 times higher than with the coaxial air-flow and electrostatic technology. © 2008 Institute of Chemistry, Slovak Academy of Sciences.
2008
U., Prüsse; L., Bilancetti; M., Bučko; B., Bugarski; J., Bukowski; P., Gemeiner; D., Lewińska; V., Manojlovic; B., Massart; Nastruzzi, Claudio; V., Nedovic; D., Poncelet; S., Siebenhaar; L., Tobler; A., Tosi; A., Vikartovská; K., Vorlop
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/1683337
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 125
  • ???jsp.display-item.citation.isi??? 108
social impact