Granular films of composition Ag70Fe30 and Ag74Fe26 were prepared by dc plasma sputtering deposition in Ar atmosphere on Si substrates. Magnetization and magnetoresistance were measured between 2 K and 270 K. Both films exhibit a negative magnetoresistance (MR). The MR vs. reduced magnetisation curves are characterised by a box-like behavior, as already observed in magnetic systems with competing interactions. A standard analysis indicates that in both systems individual Fe nanoparticles are magnetically correlated over large distances.
Proximity magnetoresistance in Ag70Fe30 and Ag74Fe26 cosputtered granular films
DA RE, Andrea;SPIZZO, Federico;
2004
Abstract
Granular films of composition Ag70Fe30 and Ag74Fe26 were prepared by dc plasma sputtering deposition in Ar atmosphere on Si substrates. Magnetization and magnetoresistance were measured between 2 K and 270 K. Both films exhibit a negative magnetoresistance (MR). The MR vs. reduced magnetisation curves are characterised by a box-like behavior, as already observed in magnetic systems with competing interactions. A standard analysis indicates that in both systems individual Fe nanoparticles are magnetically correlated over large distances.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.