The thermal evolution process of a Ta2O5 thin film from a TaCl5 precursor was followed by thermogravimetry combined with mass spectrometry. The TaCl5 coating was prepared by the deposition of dissolved TaCl5 (in 2-propanol) onto a titanium metal support. After evaporation of the solvent, the gel-like film was heated in an atmosphere containing 20% O2 and 80% Ar to 600 °C. Mass spectrometric ion intensity curves show the liberation of chlorinated species in a uniform, slow process between 200 and 500 °C and in a fast reaction in the 500-600 °C range. Bonded solvent is decomposed in an oxidative cracking process between 120 and 220 °C, resulting in the formation of elemental carbon trapped in the film. Combustion of trapped carbon takes place in the 500-600 °C range resulting in the formation of CO2 gas inclusions in the quickly solidifying surface layer as evidenced by diffuse reflectance Fourier transform infrared spectrometry.

Investigation of Ta2O5 Thin Film Evolution

DE BATTISTI, Achille;
2001

Abstract

The thermal evolution process of a Ta2O5 thin film from a TaCl5 precursor was followed by thermogravimetry combined with mass spectrometry. The TaCl5 coating was prepared by the deposition of dissolved TaCl5 (in 2-propanol) onto a titanium metal support. After evaporation of the solvent, the gel-like film was heated in an atmosphere containing 20% O2 and 80% Ar to 600 °C. Mass spectrometric ion intensity curves show the liberation of chlorinated species in a uniform, slow process between 200 and 500 °C and in a fast reaction in the 500-600 °C range. Bonded solvent is decomposed in an oxidative cracking process between 120 and 220 °C, resulting in the formation of elemental carbon trapped in the film. Combustion of trapped carbon takes place in the 500-600 °C range resulting in the formation of CO2 gas inclusions in the quickly solidifying surface layer as evidenced by diffuse reflectance Fourier transform infrared spectrometry.
2001
J., Kristof; DE BATTISTI, Achille; G., Keresztury; E., Horvath; T., Szilagyi
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/1200730
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 10
social impact