Iron (III) oxide applications as anodic material in electrocatalysis and photoelectrochemical cells are currently limited by its poor electric properties. To overcome these issues, doping has been applied with some success and high-temperature (800 degrees C) treatment on fluorine doped tin oxide substrates, leading to tin-doping, is now a widely employed procedure to activate hematite anodes. In this paper we undertake a systematic investigation of the effects of tin doping on the structural, optical and electrochemical properties of hematite thin films, focusing on the anodic performance towards water splitting. To isolate the effect of doping from those of morphology and crystallinity, we devise a fabrication method based on radio-frequency magnetron sputtering yielding crystalline hematite at room temperature, thus enhancing the compatibility towards substrates and the potential for application. Doping in the range 1-12% (atomic) induces lattice distortion with cell volume increase and a substantial extension of the visible absorption range due to a band-gap narrowing of about 0.45 eV for the highest doping level. The electrode metrics are greatly improved, with a shift of up to 60 mV towards less positive overpotentials and Tafel slopes about the half of the original value. The best performance is found for a 6.2 at. % doping, with eta = 441 mV (at j = 1 mA/cm(2)) and a 48 mV/dec Tafel slope, in line with current state-of-the-art results reported for amorphous iron based catalysts. In our case tin doping leads to improved conductivity and to a decreased (up to 1 order of magnitude) interfacial charge transfer resistance, as revealed by electrochemical impedance spectroscopy.

On the effect of Sn-doping in hematite anodes for oxygen evolution

Mazzi, A.
Co-primo
;
Rudatis, P.;Caramori, S.;Bignozzi, C. A.
Ultimo
;
2016

Abstract

Iron (III) oxide applications as anodic material in electrocatalysis and photoelectrochemical cells are currently limited by its poor electric properties. To overcome these issues, doping has been applied with some success and high-temperature (800 degrees C) treatment on fluorine doped tin oxide substrates, leading to tin-doping, is now a widely employed procedure to activate hematite anodes. In this paper we undertake a systematic investigation of the effects of tin doping on the structural, optical and electrochemical properties of hematite thin films, focusing on the anodic performance towards water splitting. To isolate the effect of doping from those of morphology and crystallinity, we devise a fabrication method based on radio-frequency magnetron sputtering yielding crystalline hematite at room temperature, thus enhancing the compatibility towards substrates and the potential for application. Doping in the range 1-12% (atomic) induces lattice distortion with cell volume increase and a substantial extension of the visible absorption range due to a band-gap narrowing of about 0.45 eV for the highest doping level. The electrode metrics are greatly improved, with a shift of up to 60 mV towards less positive overpotentials and Tafel slopes about the half of the original value. The best performance is found for a 6.2 at. % doping, with eta = 441 mV (at j = 1 mA/cm(2)) and a 48 mV/dec Tafel slope, in line with current state-of-the-art results reported for amorphous iron based catalysts. In our case tin doping leads to improved conductivity and to a decreased (up to 1 order of magnitude) interfacial charge transfer resistance, as revealed by electrochemical impedance spectroscopy.
2016
Orlandi, M; Mazzi, A.; Arban, G.; Bazzanella, N.; Rudatis, P.; Caramori, S.; Patel, N.; Fernandes, R.; Bignozzi, C. A.; Miotello, A.
File in questo prodotto:
File Dimensione Formato  
pub paper.pdf

solo gestori archivio

Descrizione: versione editoriale
Tipologia: Full text (versione editoriale)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 2.86 MB
Formato Adobe PDF
2.86 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
11392_2362026_postprint_Caramori.pdf

accesso aperto

Descrizione: post print
Tipologia: Post-print
Licenza: Creative commons
Dimensione 1.97 MB
Formato Adobe PDF
1.97 MB Adobe PDF Visualizza/Apri

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2362026
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 37
  • ???jsp.display-item.citation.isi??? 34
social impact